- Chemical resistant protective layer on concrete, stone, cementitious mortars and renderings, epoxy cement, epoxy resin based products and steel
- Lining in storage tanks and silos
- Anti-corrosion coating on steel in food processing plants, sewage works, farms, agricultural enterprises, chemical and pharmaceutical facilities and beverage industry
- Solvent free
- Good mechanical and chemical resistance
- High build
- Impervious to liquids
- Easy to mix and to apply
3.75 kg drums
1.25 kg drums
RAL 7032 (pebble grey), other on request
Conformity with LEED v2009 IEQc 4.2: Low-Emitting Materials - Paints and Coatings
APPROVALS / STANDARDS
- Coating for concrete protection according the requirements of EN 1504-2:2004, Declaration of Performance 0206060100100000011008, certified by FPC Notified Body and provided with CE marking
- WRAS, test report No. M104991, 2011, Contact with water for wholesome purposes according BS 6920-1:2000
Part A: 12 months
Part B: 12 months
From date of production if stored properly.
The packaging must be stored properly in original, unopened and undamaged sealed packaging, in dry conditions at temperatures between +5 °C and +30 °C. Protected from direct sunlight.
Mixed resin ~1.37 kg/l
Density values determined at +23 °C
~ 100 %
Shore D Hardness
CS 10/ 1000/ 1000
CS 17/ 1000/ 1000
H 22/ 1000/ 1000
Tensile Adhesion Strength
> 1.5 N/mm² to concrete
Please contact Sika technical service for specific information.
max. 7 days
|max. 12 hours||+100 °C|
Part A : Part B = 3 : 1 by weight
~0.2 mm per layer
Ambient Air Temperature
+8 °C min. / +40 °C max.
Relative Air Humidity
< 80 %
+8 °C min. / +40 °C max.
Minimum 3 °C above dew point, beware of condensation
|+30 °C||~10 min|
Waiting Time / Overcoating
~ 30 hours
~ 3 days
~ 14 days
~ 10 hours
~ 2 days
~ 6 hours
~ 1 day
~ 5 days
~0.30 kg/m² per layer
The substrate must be sound, clean, dry, free from contaminants such as dirt, grease, oil, old coatings, release agents, laitance and other adhesion preventing or influencing substances.
On high absorbent, non-sound, contaminated, not cement based substrates precautions have to be taken and a suitable primer has to be used.
Concrete substrate must be prepared mechanically to achieve an open textured surface.
Weak areas in the substrate must be removed and surface defects such as blowholes and voids must be fully exposed.
All dust, loose and friable material must be completely removed from all surfaces before application of the product, preferably by brush and/or vacuum.
Open voids and blowholes need to be closed with a suitable Sika® pore filling mortar. The roughness of the substrate needs to be levelled with a suitable Sika® rendering and levelling mortar.
Steel surface must be prepared mechanically using abrasive blast cleaning. The level SSPC-SP 10 “near white metal blast cleaned” or level Sa 2 ½ according to ISO EN 12944-4 has to be achieved. Welds and joints have to be prepared according to EN 14879, part 1. After blast cleaning remove all dust dirt and blasting material. In order to maintain the surface conditions after blast cleaning air-conditioning is recommended.
Prior to mixing stir part A mechanically. When all of part B has been added to part A mix continuously for 3 minutes until a uniform mix has been achieved. Use a low speed electrical stirrer (300–400 rpm) to avoid air entrapment. To ensure proper mixing pour material into a clean container and stir again.
Apply by brush, roller or airless spray.
CLEANING OF TOOLS
Clean all tools with Thinner C immediately after use. Hardened and/or cured material can only be removed mechanically.