Product Data Sheet Show all documents

Sikadur®-55 SLV IN

Super low-viscosity, high-strength moisture-tolerant epoxy resin, crack healer, penetrating sealer and binder adhesive

Sikadur®-55 SLV IN is a 2-component, 100 % solids, moisture-tolerant, super low-viscosity, multipurpose, epoxy crack healer / penetrating sealer. It is a high-strength epoxy adhesive formulated specifically for sealing both dry and damp, existing, non-dynamic cracks and as epoxy binder for repair in hydraulic structures.

  • Super low viscosity
  • Solvent-free
  • Suitable for both, dry and damp conditions
  • Usable at low temperatures
  • Shrinkage free hardening
  • Unique, high mechanical and structural strengths
  • Hard but not brittle
  • Deep penetrating and tenacious bonding of cracks in structural concrete
  • Injectable with single component pumps
  • Can be used as epoxy binder in preparation of mortar for repair of concrete
Product Data Sheet Show all documents

Usage

Sikadur®-55 SLV IN may only be used by experienced professionals.
  • Pressure-injection of cracks in structural concrete, masonry, wood, etc.
  • Gravity-feed of cracks in horizontal concrete and masonry
  • Epoxy resin binder for epoxy mortar patching and overlay of interior, horizontal surfaces
  • Seal interior slabs and exterior above-grade slabs from water, chlorides and mild chemical attack; also improves wearability
 

Advantages

  • Super low viscosity
  • Solvent-free
  • Suitable for both, dry and damp conditions
  • Usable at low temperatures
  • Shrinkage free hardening
  • Unique, high mechanical and structural strengths
  • Hard but not brittle
  • Deep penetrating and tenacious bonding of cracks in structural concrete
  • Injectable with single component pumps
  • Can be used as epoxy binder in preparation of mortar for repair of concrete

Packaging

Part A+B pre-batched

0.9 kg × 4 sets

Part A

0.7 kg container

Part B

0.2 kg container

Colour

Part A+B mixedClear pale yellow liquid

Part A

Colourless liquid

Part B 

Amber coloured liquid

Product Details

Product Information

Product declaration

Conforms to ASTM C881, Type I & IV, Grade 1, Class C, except for gel time

Chemical base

Epoxy resin

Shelf life

12 months from date of production

Storage conditions

The product must be stored properly in unopened, undamaged and sealed original packaging, in dry conditions at temperatures between +4 °C and +40 °C.

Density

1.15 ± 0.05 kg/L (Part A+B mixed, +25 °C)

(EN ISO 2811-1)

Viscosity

Temperature

Viscosity

+15 °C~700 Cps
+25 °C~350 Cps
Technical Information

Compressive strength

Curing timeCuring temperature

Neat Resin

Mortar (Neat Resin : Powder = 1 : 5)

1 d

+15 °C≥ 10 N/mm2≥ 40 N/mm2

3 d

+15 °C≥ 65 N/mm2≥ 65 N/mm2
7 d+15 °C≥ 70 N/mm2≥ 70 N/mm2
14 d+15 °C≥ 80 N/mm2≥ 75 N/mm2
28 d+15 °C≥ 85 N/mm2≥ 80 N/mm2

   

Curing timeCuring temperature

Neat Resin

Mortar (Neat Resin : Powder = 1 : 5)

1 d

+25 °C≥ 70 N/mm2≥ 65 N/mm2

3 d

+25 °C≥ 75 N/mm2≥ 70 N/mm2
7 d+25 °C≥ 80 N/mm2≥ 75 N/mm2
14 d+25 °C≥ 85 N/mm2≥ 80 N/mm2
28 d+25 °C≥ 90 N/mm2≥ 85 N/mm2

Tensile strength

Curing time

Curing temperature

Neat ResinMortar (Neat Resin : Powder = 1 : 5)

7 d

+15 °C≥ 50 N/mm2≥ 12 N/mm2

7 d

+25 °C≥ 50 N/mm2≥ 15 N/mm2

Elongation at break

Curing time

Curing temperature

Neat ResinMortar (Neat Resin : Powder = 1 : 5)

7 d

+15 °C~2 %~0.3 %

7 d

+25 °C~2 %~0.3 %

Tensile adhesion strength

Curing time, Curing typeCuring temperatureNeat ResinMortar (Neat Resin : Powder = 1 : 5)
2 days, moist cure+15 °C≥ 7 N/mm2≥ 7 N/mm2
14 days, moist cure+15 °C≥ 10 N/mm2≥ 10 N/mm2
2 days, dry cure+25 °C≥ 7 N/mm2≥ 7 N/mm2
14 days, dry cure+25 °C≥ 10 N/mm2≥ 10 N/mm2

Heat deflection temperature

Curing time

Curing temperature

Neat Resin

Mortar (Neat Resin : Powder = 1 : 5)

7 d

+15 °C

≥ 50 °C≥ 50 °C

7 d

+25 °C≥ 50 °C≥ 50 °C

Water absorption

Curing timeNeat ResinMortar (Neat Resin : Powder = 1 : 5)

7 d

~0.25 %~0.56 %

Application

Application Information

Mixing ratio

Neat Resin

Part A : Part B = 7 : 2 (by weight)

Mortar

Part A : Part B : Part C = 7 : 2 : 45 (by weight)

Ambient air temperature

+15 °C min. / +45 °C max.

Substrate temperature

+15 °C min. / +45 °C max.

Pot life

TemperaturePot life
+15 °C~75 minutes (100 g mass)
+25 °C~24 minutes (100 g mass)
Application steps

APPLICATION INSTRUCTIONS

SUBSTRATE QUALITY

  • The surface to be treated must be structurally sound, free from standing water, oil, grease, surface contaminants.
  • Minimum age of concrete must be 21 - 28 days, depending on curing and drying conditions.

SUBSTRATE PREPARATION

  • Concrete, mortar, stone should be thoroughly prepared.
  • Dirt, dust and other foreign materials must be removed by high pressure water jetting or mechanical means such as grinding, chiselling etc.
  • Concrete which is fully contaminated with oil / grease, must be removed to the depth of sound & uncontaminated concrete.
  • Cracks must be cleaned to remove dust with compressed air.

MIXING

Neat resin or primer

  1. Weigh the resin (comp. A) and hardener (comp. B) part as per mixing ratio (by weight) and mix together for 3 minutes at slow speed (400-500 rpm) with a mixing spindle attached to an electrical drill.
  2. Continue mixing until the material becomes uniform in colour. Avoid aeration while mixing. Mix only that quantity which can be used within its pot life. 

  

Mortar system

  1. To prepare an epoxy mortar slowly add 5 parts by weight of filler (comp. C) to 1 part of mixed Part A + Part B and mix until uniform in consistency.

APPLICATION

Strictly follow installation procedures as defined in method statements, application manuals and working instructions which must always be adjusted to the actual site conditions.

  

IMPORTANT

Sikadur®-55 SLV IN is not designed for injection / impregnation of cracks under hydrostatic pressure at the time of application.

IMPORTANT

Do not seal exterior slabs on grade.

  

Impregnation of cracks in horizontal planes:
Saturate the crack by applying the product by paint brush or roller in several passes or by pouring between two "barriers" made with Sikaflex® sealant. The crack penetrating through structure must be sealed on the underside with Sikadur®-31 IN epoxy mortar or a suitable Sika® cementitious mortars.

  
Injection of cracks on horizontal / vertical planes:
Sikadur®-55 SLV IN can be injected under pressure into cracks using a single-component injection pump. The injectors should be placed at a distance of 25 cm and the fissure between sections of injectors should be superficially sealed with Sikadur®-31 to avoid the loss of resin during the injection process. Vertical cracks must be injected from the bottom up. As soon as the resin oozes through the next injector, the first must be sealed and continue the injection process from the next. After completing the injection process, the injectors and sealing material can be removed.

  

IMPORTANT

Maximum width of cracks to be injected: 5 mm. Please contact Sika Technical Services for cracks > 5 mm.

  

Mortar Application

  1. Prime prepared surface with mixed Part A & Part B of Sikadur®-55 SLV IN.
  2. Place prepared epoxy mortar before primer becomes tack-free using trowels.
  3. Finish with finishing trowel.

IMPORTANT

Maximum epoxy mortar thickness is 25 mm per layer.

CLEANING OF TOOLS

Clean all tools and application equipment with Sika® Colma-Cleaner or good quality N C thinner immediately after use. Hardened or cured material can only be mechanically removed.