Sika® Polysulphide, Pour Grade

Two component polysulphide sealant - Pour grade

Sika® Polysulphide, Pour Grade is a two component Polysulphide sealant. It is used for sealing expansion joints where large movement is anticipated in concrete construction and for joints between diverse construction materials. It is suitable for sealing joints subjected to vehicular traffic and is chemically resistant to water, fuels, oils and solvents.

  • Excellent adhesion with most common construction materials
  • Resistant to UV and weathering in exposed conditions
  • High movement accommodation
  • Good chemical resistance
  • Permanently elastic and forms watertight seal
  • Flame and fuel resistant
  • Easy to use
  • Economical
Product Data Sheet Show all documents

Usage

Wherever a permanently flexible seal is required, it is used in horizontal expansion joints in many types of buildings and civil engineering constructions such as
  • Precast concrete elements
  • Dams, Reservoirs and water treatment plants
  • Residential & Commercial buildings
  • Subways, bridges, culverts, tunnels
  • Rigid pavements of highways, airport runways, aprons, etc
 

Advantages

  • Excellent adhesion with most common construction materials
  • Resistant to UV and weathering in exposed conditions
  • High movement accommodation
  • Good chemical resistance
  • Permanently elastic and forms watertight seal
  • Flame and fuel resistant
  • Easy to use
  • Economical

Packaging

Part A : 3.68 kg, Part B : 0.32 kg, Total : 4 kg

1 Box = 4 kg x 2 sets

Colour

Grey Paste

Product Details

Sustainability / Certifications / Approvals

APPROVALS / STANDARDS

Conforms to

BS 4254 - 1983

BS 5212 - 1990

IRC : 57 - 2006

IS : 12118 (Part 1)

JIS K 6820
Product Information

Chemical Base

Cross linking polysulphide

Shelf Life

12 months in unopened condition from the date of production

Storage Conditions

Store properly in unopened, undamaged original packaging in cool and dry condition at temperature +5°C to + 25°C at a Relative Humidity of 50%

Density

1.6 -1.75 kg/litre at 30°C

(JIS K6820)
Technical Information

Shore A Hardness

11 ± 3

(ASTM D 2240)

Elongation

≥ 450%

(ASTM D882)

Elastic Recovery

Before Ageing

> 75%

After Heat Ageing (70 °C / 14 days)

> 75%

After fuel immersion (48 hrs)

> 75%

Movement Capability

Test Condition

Specified Value

Observed Value

30% Extension/RT/24 hrs with 1hr Relaxation

No Cohesive & Adhesive Failure

 Passes the Test

30% Compression/RT/24 hrs with 1hr Relaxation

No Cohesive & Adhesive Failure

Passes the Test

Resistance to Fire

Pass (Flame Resistance Test)

(BS 5212-1990)

Service Temperature

- 40°C to  + 80°C

Joint Design

The product may be applied to joint between 5 to 50 mm wide. Joints subjected to cyclic movements should be designed for an optimum Width/Depth ratio of 2 : 1 (W = 2D).

Type Of Substrate

Minimum Joint Depth(mm)

Metals, glass and other non-porous surfaces.

5mm

Brick,Concrete and other porous surfaces

10mm

Trafficable joints and those subject to hydraulic pressures.20mm

Application

Application Information

Mixing Ratio

Part A : Part B , 92 : 8 (by weight)

Ambient Air Temperature

+5°C min. / +45°C max.

Substrate Temperature

+5°C min. / +45°C max.

Substrate Moisture Content

Dry joint with sound concrete edges. For joints under wet conditions, use Sika® Primer 3 IN

Pot Life

> 90 minutes at 30°C  (500g mix)

Curing Time

Type Of Curing With Time

Minimum Time Required

Basic Curing

6 hrs at 30°C for 500g mix

Sufficient curing to gain handling strength

24 hrs at 30°C

Total Cure for development of full properties7 days

Tack Free Time

16 ± 0.1 hrs

(BS 5212-1990)

Application Time

> 30 minutes
Application steps

SUBSTRATE PREPARATION

  • All surfaces must be clean, dry and free from any loosely adhering particles.
  • Check the joints edges for soundness and if found weak cut recess and fill up with suitable repair mortar (Consult Sika® Technical services).
  • Correct joint depth can be established by inserting polyethylene based Sika® Backer Materia,glass rod,etcl tightly into the joint. When the joints have been filled with fibre filled board, this must be raked back to the required depth. Use bond breaker tape over the backer material. Protect surfaces with masking tape.
  • Sika® Primer 3 IN/Sika® Primer 3 should be used as a primer only on the two sides. Allow a flash-off time of at least 45 minutes before sealant application (maximum 4 hours).  

MIXING

The two components are mixed in the ratio Comp A : Comp B = 92 : 8 by weight with a low speed mixer (300 - 600 rpm). Mix for approximately 8 - 10 minutes until a smooth, even consistency is achieved.

CLEANING OF TOOLS

Clean all tools and application equipment with Solvent immediately after use. Hardened / cured material can only be mechanically removed.