Sikadur-Combiflex® Adhesive IN
Sikadur-Combiflex® Adhesive IN is a 2-part epoxy based thixotropic adhesive for bonding the Sikadur-Combiflex® SG modified flexible Polyolefin (FPO) waterproofing tapes to different substrates. Internal and external use. Application temperature range +10 °C to +40 °C. It is part of the Sikadur-Combiflex® SG System.
- Easy to mix and apply
- Suitable for both dry and damp concrete surfaces
- Excellent adhesion to many materials
- Solvent free
- Performs well within a wide temperature range
- Completely weather and water resistant
- Fast curing
- Root resistant
- Good resistance to many chemicals
- Thixotropic - suitable for overhead and vertical application
- No primer needed
- High mechanical resistance
- Good abrasion resistance
Usage
Sikadur-Combiflex® Adhesive IN may only be used by experienced professionals.- Adhesive for the Sikadur-Combiflex® SG System
- Adhesive for the other Sika® Joint Sealing Systems
- Expansion Joint treatment
- Construction Joint treatment
- Crack treatment
- Precast panels joint treatment
Advantages
- Easy to mix and apply
- Suitable for both dry and damp concrete surfaces
- Excellent adhesion to many materials
- Solvent free
- Performs well within a wide temperature range
- Completely weather and water resistant
- Fast curing
- Root resistant
- Good resistance to many chemicals
- Thixotropic - suitable for overhead and vertical application
- No primer needed
- High mechanical resistance
- Good abrasion resistance
Packaging
Part A+B pre-batched | 6 kg set |
Part A | 4 kg container |
Part B | 2 kg container |
Colour
Part A+B mixed | Concrete grey |
Part A | White |
Part B | Black |
Product Details
Chemical base
Epoxy resin and selected fillers
Shelf life
12 months from date of production
Storage conditions
The product must be stored in original, unopened and undamaged sealed packaging in dry conditions at temperatures between +5 °C and +40 °C.
Density
~1.6 kg/L (Part A+B mixed, +30 °C) | (EN ISO 2811-1) |
System structure
Refer to Sikadur-Combiflex® SG System data sheet or contact Sika Technical Services for specific information.
Compressive strength
Curing time (+30 °C) | Compressive strength |
3 day | 50 N/mm2 |
7 days | 55 N/mm2 |
Tensile adhesion strength
Substrate | Adhesion strength |
Concrete (dry) | > 2 N/mm2 * |
Concrete (mat damp) | > 2 N/mm2 * |
Steel (blast cleaned) | > 2 N/mm2 |
* failure in concrete
Chemical resistance
Refer to Sikadur-Combiflex® SG System system data sheet or contact Sika Technical Services for specific information.
Application
Mixing ratio
Part A : Part B = 2 : 1 (by weight)
Ambient air temperature
+10 °C min. / +40 °C max.
Dew point
Beware of condensation.
Steel substrate temperature during application must be at least +3 °C above dew point.
Substrate temperature
+10 °C min. / +40 °C max.
Substrate moisture content
Cementitious substrates:
Substrate must be dry or matt damp (no standing water).
Brush the adhesive well into the substrate if matt damp.
Pot life
~30 minutes (100 g mass, +30 °C)
If larger quantities are being mixed the temperature of Sikadur-Combiflex® Adhesive IN will increase due to the chemical reaction, resulting in a reduced pot life.
Waiting time / Overcoating
Sikadur-Combiflex® Adhesive IN may be overcoated with an epoxy coating. If this is required, do not smooth the adhesive with detergent. If waiting time between application of adhesive and overcoating is to be longer than 2 days, the adhesive must be blinded to excess with quartz sand immediately after application.
Consumption
Tape width | Tape thickness | Consumption * |
150 mm | 1 mm | 1.0 kg/m |
200 mm | 1 mm | 1.2 kg/m |
250 mm | 1 mm | 1.4 kg/m |
150 mm | 2 mm | 1.1 kg/m |
200 mm | 2 mm | 1.4 kg/m |
250 mm | 2 mm | 1.7 kg/m |
* The effective consumption can vary depending on site conditions (surface roughness, size of aggregate etc.).
SUBSTRATE QUALITY
Concrete/masonry/mortar/stone
Concrete and mortar must be at least 3–6 weeks old.
Substrate surfaces must be sound, clean, dry or matt damp, free from standing water, ice, dirt, oil, grease, coatings, laitance, efflorescence, old surface treatments, all loose particles and any other surface contaminants that could affect adhesion of the adhesive.
Steel
Surfaces must be clean, dry, free from oil, grease, coatings, rust, scale, all loose particles and any other surface contaminants that could affect adhesion of the adhesive.
SUBSTRATE PREPARATION
Concrete/masonry/mortar/stone
Substrates must be prepared mechanically using suitable abrasive blast cleaning, needle gunning, light scabbling, bush hammering, grinding or other suitable equipment to achieve an open textured gripping surface profile.
Steel
Surfaces must be prepared mechanically using suitable abrasive blast cleaning, grinding, rotating wire brush or other suitable equipment to achieve a bright metal finish with a surface profile similar to aluminium oxide paper medium grade. Avoid dew point conditions before and during application.
All substrates
All dust and loose material must be completely removed from all substrate surfaces before application of the product by vacuum / dust removal equipment.
MIXING
IMPORTANT
Avoid over mixing to minimise air entrainment.
IMPORTANT
Mix full units only.
Note: Use a spiral paddle in an electric single paddle mixer at a maximum speed of 500 rpm.
- Mix Part A (resin) for ~60 seconds.
- Add Part B (hardener) to Part A (resin).
- Mix Parts A+B continuously for ~2 minutes until a uniformly smooth, coloured mix is achieved.
- To ensure thorough mixing, pour materials into another clean container and mix again for 1 minute to achieve a smooth and uniform mix.
APPLICATION
- Apply the mixed product by hard brush or trowel.
For detailed application method, please refer Sikadur-Combiflex® SG System data sheet and Sika Method Statement.
CLEANING OF TOOLS
Clean all tools and application equipment with Sika® Colma-Cleaner immediately after use. Hardened or cured material can only be removed mechanically.