Product Data Sheet Show all documents

SikaTop®-107 Seal IN

TWO PACK POLYMER MODIFIED CEMENTITIOUS WATERPROOFING SLURRY AND PROTECTIVE COATING

SikaTop®-107 Seal IN is a two part acrylic polymer modified cementitious liquid applied waterproofing coating system. It comprises of a liquid polymer and a cement based mix incorporating special admixtures. It is applied to concrete and mortar to prevent water infiltration.

  • Easy to apply by brush or in thin trowel applications
  • No additional water is required to make the slurry
  • Pre batched components with consistent quality
  • Hand or Spray applied
  • Easy and fast mixing
  • Increased frost and salt resistance
  • Very good adhesion with sound and prepared substrates
  • Protects concrete against water penetration, chloride and carbonation
  • Non Corrosive to steel and iron
  • Approved for potable water contact
  • Flexible enough to bridge hairline crack
  • Bonds well to all damp substrates
  • Can be applied on reinforced concrete, mortar or masonary
Product Data Sheet Show all documents

Usage

  • Interior and exterior waterproofing and damp-proofing of concrete, cementitious rendering, brickwork and blockwork
  • Protection of concrete structures against the effects of de-icing salts and freeze-thaw attack
  • Exterior waterproofing of basement walls in new construction and refurbishment
  • Pore / blowhole filling
  • Rigid waterproofing of water tanks, bathrooms, toilets, etc.
  • Sealing fine “hairline” cracks in concrete structures not subject to movement
  • Sealing internal basement walls against dampness
  • Levelling mortar for concrete repair works
  Areas of application
  • Potable concrete water tanks / reservoirs
  • Terraces and balconies
  • Flat and small roofs
  • Basement and Retaining walls
  • Swimming pools, fountains and water bodies
  • RCC gutters, drains and planter boxes
  • Bathroom / toilets / Sunk slabs
  • Lift pits / Sump
  • Seawalls
 

Advantages

  • Easy to apply by brush or in thin trowel applications
  • No additional water is required to make the slurry
  • Pre batched components with consistent quality
  • Hand or Spray applied
  • Easy and fast mixing
  • Increased frost and salt resistance
  • Very good adhesion with sound and prepared substrates
  • Protects concrete against water penetration, chloride and carbonation
  • Non Corrosive to steel and iron
  • Approved for potable water contact
  • Flexible enough to bridge hairline crack
  • Bonds well to all damp substrates
  • Can be applied on reinforced concrete, mortar or masonary

Packaging

Part A: 5.0 kg container

Part B: 20.0 kg bag

Part (A+B) : 25 kg ready to mix units x 2 sets

Colour

Part A : White Liquid
Part B : Grey Powder
Part A+B : Cement Grey slurry

Product Details

Sustainability / Certifications / Approvals

APPROVALS / STANDARDS

  • SGS Certificate - Free from acute lethal toxicity as per IS 6582
  • CFTRI Certificate for repeated use with aqueous foods / water as per USFDA 175.300
     
Product Information

Chemical Base

Part A : Liquid polymer & additive
Part B : Portland Cement with selected aggregate and additive

Shelf Life

12 months from date of production

Storage Conditions

Product should be stored in original, unopened, undamaged and sealed packaging in dry and cool conditions. Liquid component must be protected from frost.

Density

Fresh Slurry : ~ 2.0 kg/ liter at +27°C
System information

System Structure

Base Coat : 1 x SikaTop®-107 Seal IN
Fabric reinforcement : 1 x Sika® Fab-1
Top Coat : 1 x SikaTop®-107 Seal IN
Technical Information

Compressive Strength

3 days

≥ 2 N/mm2

28 days

≥ 20 N/mm2

At temperature +27°C

Tensile Strength

≥ 4.5 N/mm² after 14 days exposure

(ASTM D 2370)

Tensile Adhesion Strength

≥ 2 N/mm² (Concrete Failure)

(ASTM C 882)

Application

Application Information

Mixing Ratio

Part A : Part B = 1:4 (By weight)

Layer Thickness

1.5 – 2.0 mm average thickness with Sika® Fab-1

Ambient Air Temperature

+10°C min. / +40°C max.

Substrate Temperature

+10°C min. / +40°C max.

Pot Life

~ 40 minutes at +27°C. Pot life will be shortened at higher temperatures.

Waiting Time / Overcoating

Waiting Time
The waiting time between coats is 2 - 6 hours (at +30°C).

  

Overcoating
For overcoating with cementitious materials, allow the second coat to harden for at least 3 days prior to overcoating.
For use in water-retaining structures or for applying renders over it or for overcoating with non-cementitious materials, please contact Sika Technical Services.
Consumption

Consumption

Layer

Product

Consumption

1

SikaTop®-107 Seal IN

~ 1.5 kg/m2

2

Sika® Fab-1

~1 m2/m2

3

SikaTop®-107 Seal IN

~ 1.5 kg/m2

  • Actual site consumption is dependent on the application area, substrate roughness, surface profile and thickness required
  • Depending on the type of application, 2 coats are always required.
  • For waterproofing upto 1m head pressure ~1.5 kg/m2 per coat.
  • Above 1m head pressure ~ 2 kg/m2 per coat.
  • Three coats may be required in areas of extremely high infiltration.
  • Normally 3 kg/m2 of SikaTop®-107 Seal IN is sufficient to cover one square meter area. On well prepared smooth substrate the consumption would be less.
  • Usage of Sika® Fab-1 is optional. For application areas, where Sika® Fab-1 is must, please consult Sika Technical Services.
Application steps

EQUIPMENT

SikaTop®-107 Seal IN must be mechanically mixed using a forced action mixer or in a clean drum using a drill and paddle (max. 500 rpm). A normal concrete free fall mixer is NOT suitable.

MIXING

The consistency of the mix can be altered by reducing the amount of Component A (liquid) to be used. Under normal circumstances, when the full quantities of both components are mixed together, a slurry consistency will result. For trowellable consistency use only 90% of component A. Mix in a clean container by slowly adding the powder component to the liquid component and stirring with low speed mixer (max. 500 rpm). Mix for 3 minutes until free from lumps.

APPLICATION

The surface must be pre-wetted to a saturated surface dry condition with no standing water at time of application. While the surface is still damp from saturation, apply the first coat and leave to harden for 2-6 hrs at +30°C before applying the second coat.

 

As a slurry
Apply the mixed SikaTop®-107 Seal IN by hand using a hard plastic bristled brush or broom. Applied in the same direction. Apply the second coat of SikaTop®-107 Seal IN in crosswise direction to the first application as soon as first coat has hardened.
 

As a mortar
SikaTop®-107 Seal IN is applied by trowel (e.g. for a smooth surface finish), the product must be mixed with a 10 % reduction of part A. Apply the second coat of SikaTop®-107 Seal IN as soon as the first coat has hardened.
For pore / blowhole filling, tightly trowel into the pores / blowholes of the surface.
For floor applications, to avoid risk of damage to the first coat, it is recommended that the second coat be applied before 24 hours. If the second coat is applied 12 hours or later, the first coat shall be slightly prewetted, preferably by using a fine spray. After the second coat has been applied, a better finish can be achieved by rubbing down with a soft, dry sponge. For more details, please contact Sika Technical Services.

CURING TREATMENT

For cement based products, proper curing is important for minimum 3 to 5 days.
Protect newly applied SikaTop®-107 Seal IN against direct sunlight, wind, rain and frost to ensure full cement hydration and minimise cracking. Use polythene sheeting or similar approved methods.

CLEANING OF TOOLS

Clean all tools and application equipment with clean water immediately after use. Hardened / cured material can only be removed mechanically.